LOCTITE PC 6311
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Heavy-Vehicular Non-Slip Coating
- 8.9:1 Volume Mix Ratio
- 1.05 Dry and Wet Friction
Product Description
LOCTITE PC 6311 is a two-component epoxy non-slip coating for industrial floors and decks exposed to heavy vehicular traffic. Resin and hardener mix at 17.6:1 by weight or 8.9:1 by volume and cure at room temperature. Typical uncured volume solids is 70%. Application methods include roller, spray, or trowel. At 21 deg C, light pedestrian dry time is 12 hours and heavy pedestrian dry time is 48 hours. After cure at 21 deg C, typical ASTM F609 coefficient of friction is 1.05 in both dry and wet tests. Typical dry service temperature is -30 to 60 deg C.
Key features
- 8.9:1 Volume Mixing: The resin-to-hardener ratio is 8.9:1 by volume and 17.6:1 by weight.
- Typical 70% Volume Solids: Typical uncured volume solids is 70%.
- 1.05 Dry and Wet Friction: Typical ASTM F609 coefficient of friction is 1.05 in both dry and wet tests after cure at 21 deg C.
Applications
Industrial floor and deck areas exposed to heavy vehicular traffic, including concrete or steel ramps, walkways, and loading docks.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Other Properties
Additional Information
As supplied
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Mix ratio | 8.9:1 | Resin:hardener by volume | |
| Mix ratio | 17.6:1 | Resin:hardener by weight | |
| Volume solids | 70 | % | Typical; uncured material |
| VOC | 250 | g/L | Typical; uncured material |
| Coverage | 3.7 | m^2 per 3.78 L | Typical; roller application |
| Coverage | 5.6 | m^2 per 3.78 L | Typical; spray application |
| Coverage | 4.6 | m^2 per 3.78 L | Typical; trowel application |
Cured coating
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Coefficient of friction - dry | 1.05 | Typical; ASTM F609; cured at 21 deg C | |
| Coefficient of friction - wet | 1.05 | Typical; ASTM F609; cured at 21 deg C | |
| Dry service temperature | -30 to 60 | deg C | Typical; heavy vehicular traffic application |