LOCTITE PC 6249
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- No-Mix Epoxy Application
- Multi-Method Floor Coating
- At Least 0.8 Wet Friction
Product Description
LOCTITE PC 6249 is a one-component epoxy non-slip floor and deck coating for concrete and steel areas with heavy pedestrian or light rolling traffic. Typical uncured volume solids is 62%. Application methods include roller, spray, or trowel. At 21 deg C, light pedestrian dry time is 12 hours and heavy pedestrian dry time is 72 hours, while tack-free time is up to 6 hours. After cure at 21 deg C, typical ASTM F609 coefficient of friction is at least 1.0 dry and at least 0.8 wet. The coating is used on ramps, walkways, loading docks, and similar floor or deck surfaces where a non-slip finish is required.
Key features
- 62% Typical Volume Solids: Typical uncured volume solids is 62%.
- Roller, Spray, or Trowel Application: Application methods include roller, spray, and trowel.
- ASTM F609 Friction: After cure at 21 deg C, typical coefficient of friction is at least 1.0 dry and at least 0.8 wet.
Applications
Ramps, walkways, loading docks, and similar concrete or steel floor and deck surfaces.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Other Properties
Additional Information
As supplied
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Volume solids | 62 | % | Typical; uncured material |
| Coverage | 4.6 | m^2 per 3.78 L | Typical; roller application |
| Coverage | 5.6 | m^2 per 3.78 L | Typical; spray application |
| Coverage | 3.7 | m^2 per 3.78 L | Typical; trowel application |
| Sag resistance | 2 | mm | Typical; no sagging; uncured material |
Cured coating
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Coefficient of friction - dry | At least 1.0 | Typical; ASTM F609; cured at 21 deg C | |
| Coefficient of friction - wet | At least 0.8 | Typical; ASTM F609; cured at 21 deg C | |
| Impact resistance | 50 | cm*kg | Typical; cured at 21 deg C |
| Flexibility | Up to 100 | mm | Typical; cured at 21 deg C |
| Water resistance | No swelling, foaming, or flaking | Typical; 15 days; cured at 21 deg C |