LOCTITE EA E-05MR
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Matched 1:1 Volume or Weight Mixing
- Fast 10 to 15 Minute Fixture
- Ultra-Clear Impact-Resistant Bonding
Product Description
LOCTITE EA E-05MR is a two-part, medium-viscosity epoxy adhesive that develops an ultra-clear, impact-resistant bondline through room-temperature cure. Resin and hardener mix 1:1 by volume or weight, with a 7 to 12 minute gel time at 22 deg C and a 10 to 15 minute fixture time on grit-blasted steel. The gap-filling adhesive is used on rough or poorly fitting surfaces and bonds supported materials including metals, ceramics, rigid plastics, and wood. Cured material combines high tensile strength with dielectric performance, making the clear system useful for general-purpose structural bonding where appearance and impact resistance matter.
Key features
- Equal-Ratio Epoxy Mixing: Resin and hardener mix 1:1 by volume or weight.
- Steel Fixture Time: Fixture time on grit-blasted steel is 10 to 15 minutes at 22 deg C under ISO 4587.
- Impact-resistant clear bondline: Room-temperature cure forms an ultra-clear bondline with excellent impact resistance.
Applications
Applications include general-purpose bonding of supported metal, ceramic, rigid plastic, and wood substrates, including rough or poorly fitting surfaces.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Thermal Properties
Mechanical Properties
Other Properties
Additional Information
As-supplied / before-processing properties
Component and mixed-material values are identified in the Method / condition column.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Viscosity | 18,000 to 25,000 | mPa s | Resin; cone and plate at 25 deg C and 100 s^-1 |
| Viscosity | 18,000 to 25,000 | mPa s | Hardener; cone and plate at 25 deg C and 100 s^-1 |
| Specific gravity | 1.16 | Mixed material at 25 deg C | |
| Mix ratio | 1:1 | by volume | Resin:hardener |
| Mix ratio | 1:1 | by weight | Resin:hardener |
| Gel time | 7 to 12 | minutes | Mixed material at 22 deg C |
| Fixture time | 10 to 15 | minutes | ISO 4587; grit-blasted steel; 22 deg C |
After-processing / final-state properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Glass transition temperature | 39 | deg C | ISO 11359-2; cured 5 days at 22 deg C |
| Hardness | 78 | Shore D | ISO 868; cured 5 days at 22 deg C |
| Dielectric breakdown strength | 34 | kV/mm | IEC 60243-1; cured 5 days at 22 deg C |
| Tensile strength | 50 | N/mm^2 | ISO 527-3; cured 3 days at 22 deg C |
| Elongation | 4.5 | % | ISO 527-3; cured 3 days at 22 deg C |
| Lap shear strength | 23 | N/mm^2 | ISO 4587; grit-blasted steel; 0.13 mm gap; cured 5 days at 22 deg C |