KANEKA GR6810
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- Toughened Compression-Molding Performance
- Fast 30-Minute Cure Cycle
- Sporting-Goods Composite Manufacturing
Product Description
Kaneka GR6810 is a toughened epoxy composite resin grade for wet lamination and compression molding. Initial viscosity is 4,300 cP at 77 deg F, and the cure schedule is 30 minutes at 180 deg F. Cured-system data include a 170 deg F (77 deg C) glass transition temperature, 131 MPa flexural strength, and 3.0 GPa flexural modulus. Applications include sporting-goods manufacturing for snow skis and snowboards. This product is the epoxy resin grade only; a curing agent is not included.
Key features
- Toughened composite resin: The epoxy grade is formulated for wet lamination and compression molding.
- Fast cure profile: The cure schedule is 30 minutes at 180 deg F.
- Sporting-goods production: Applications include manufacturing snow skis and snowboards.
Applications
Wet lamination and compression molding for sporting goods, including snow skis and snowboards.
TDS, SDS & Technical Documents
Technical Specifications
Physical Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
Values are product-selection data for the resin grade and are not specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Resin type | Epoxy | As supplied | |
| Initial viscosity | 4,300 | cP | 77 deg F |
| Cure schedule | 30 | min | 180 deg F |
After-processing / final-state properties
Values describe cured-system performance and are product-selection data, not specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Glass transition temperature | 170 (77) | deg F (deg C) | Cured system |
| Flexural strength | 131 | MPa | Cured system |
| Flexural modulus | 3.0 | GPa | Cured system |