ELANTAS AD-1147-1
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- Brush, Spray, Roller, or Doctor-Blade Application
- 82 to 93 deg C Heat Activation
- 0.5 to 1.5 mil Dry Film
Product Description
CONAP AD-1147-1 Adhesive Primer is a red solvent-borne, heat-activated primer for bonding liquid polyurethanes to metal, glass, composite, wood, and leather substrates. Typical viscosity is 1,500 to 2,750 cP at 25 deg C with 23 to 25% solids and a weight of 7.50 lb/gal. The primer can be applied by brush, spray, roller coating, or doctor blade. For AD-1147-1, the TDS calls for one or two coats, air drying between coats, then heat activation at 82 to 93 deg C for 1 to 2 hours before polyurethane application. Recommended dry film thickness is 0.5 to 1.5 mil.
Key features
- 1500 to 2750 cP Viscosity at 25 deg C: The range applies to the as-supplied adhesive primer at 25 deg C.
- 82 to 93 deg C Heat Activation: The primer is heated for 1 to 2 hours before polyurethane application.
- 23 to 25% Solids Content: The range applies to the as-supplied primer.
Applications
Bonding liquid polyurethanes to aluminum alloys, magnesium, iron, steel, glass, glass-fiber laminates, wood, and leather.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Viscosity | 1,500-2,750 | cP | 25 deg C; AD-1147-1; typical |
| Solids | 23-25 | % | 1 g sample; 3 hours at 105 deg C; AD-1147-1; typical |
| Weight | 7.50 | lb/gal | 25 deg C; AD-1147-1; typical |
| Appearance | Red | - | AD-1147-1 |
| VOC | 5.7 | lb/gal | ASTM D3960; AD-1147-1; typical |